Purpose: To evaluate the bond strength to dentin produced by experimental adhesives formulated with an elastomeric methacrylate monomer (EMM) and an alternative initiator system based on a Thioxanthone derivative (QTX). Materials and Methods: A self-etching primer was used. For the bonding resin, a model adhesive (G1) was formulated containing bis-GMA/TEG-DMA/HEMA (co-monomeric blend) + CQ/EDAB (initiator system). The other groups were formulated by adding to this formulation: EMM only (G2), QTX (G3), or EMM and QTX (G4). Clearfil SE Bond was used as the commercial control group. Fifty bovine teeth (n = 5) were restored with each one of the five adhesives. After restorative procedures, half of the specimens were stored in distilled water at 37°C for 24 h. The other half was fixed on a metal stub and subjected to 200,000 mechanical (50 N loading at 2 Hz frequency) and 1000 thermal cycles (5°C and 55°C). Afterwards, specimens were serially sectioned into beams and tested in tension until fracture. Bond strengths were statistically analyzed by two-way ANOVA and Tukey's test (α = 5%). Results: After 24 h, significantly higher µTBS was observed for the formulation containing EMM and QTX (G4) when compared to Clearfil SE Bond (p 0.05). No significant differences in µTBS were detected among the experimental groups after 24 h (p>0.05). After thermomechanical cycling, no significant differences were observed among groups. Conclusion: The addition of EMM and QTX can be considered as possible alternative in dental adhesive formulations. Schlagwörter: adhesives, microtensile bond strength, thermomechanical load cycling, thioxanthone