Purpose: This study was undertaken to evaluate ion beam-assisted deposition (IBAD) of hydroxyapatite (HA) on the grit-blasted surface of endosseous dental implants 6 weeks postplacement. Materials and Methods: A total of 40 implants was placed in the tibiae of 10 New Zealand white rabbits. Twenty implants were grit-blasted only and the other 20 were grit-blasted and coated with HA by the IBAD method. After 6 weeks of healing, the rabbits were sacrificed and removal torque tests, histomorphometry, and morphometric analysis of microtomographic images were performed. Results: The HA-coated group showed significantly higher removal torque, bone-to-implant contact, and bone volume than the other group. Discussion and Conclusion: In a previous study, the authors suggested that HA coating deposited on a machined surface by the IBAD method showed results comparable to or more favorable than the results obtained with a blasted surface. This study indicated that the HA coating produced by the IBAD method was also very effective on the aluminum oxide-blasted surface, as demonstrated by the early formation of osseointegration. Morphometric analysis by microtomography showed some promise in measuring the osseointegration rate. (More than 50 references.)