Purpose: To compare the color dimensions, color discrepancies (ΔE00), and surface roughness of milled materials before and after application of a bleaching agent. Materials and Methods: A total of 10 extracted molars were obtained. Each tooth was cut in transverse sections to create disks (3-mm thick, 10-mm diameter; control group). Disk specimens of eight materials (n = 10 per group) were fabricated: polymethyl methacrylate (PMMA) interim material (PMMA-Telio group), two resin nanoceramics (RNC-Ultimate group and RNC-Cerasmart group), two hybrid ceramics (HC-Shofu group and HC-Enamic group), lithium disilicate (LD-Emax group), zirconia-reinforced glass ceramic (ZGC-Suprinity group), and zirconia (Zr-InCeram group). Color measurements were obtained using a spectrophotometer before and after applying 35% hydrogen peroxide–based bleaching agent. Pre- and postbleaching surface roughness (Sa) analyses were completed using a profilometer. Results: Significant L*, a*, b*, and ΔE00 value differences were found (P < .05). Color discrepancies (ΔE00) ranged from 0.30 ± 0.14 to 4.82 ± 0.10. The highest color discrepancies were measured on the PMMA-Telio group, while the lowest color discrepancies were computed for ZGC-Suprinity, RNCUltimate, and RNC-Cerasmart. Significant surface roughness differences were found (P < .05). The largest increase of surface roughness values between the pre- and postbleaching measurements was obtained in the PMMA-Telio group with a mean ΔSa value of 4.73 ± 3.02, while the largest decrease of surface roughness values between the pre- and postbleaching measurements was obtained in the Zr-InCeram group with a mean ΔSa value of –1.58 ± 0.10. Conclusions: The milled materials showed significant pre- and postbleaching color and surface roughness discrepancies.