DOI: 10.3290/j.jad.a8427Pages 153-162, Language: EnglishSahafi, A. / Peutzfeldt, Anne / Asmussen, E. / Gotfredsen, K.To determine the effect of surface treatments on bond strength of two resin cements (ParaPost Cement and Panavia F) to posts of titanium alloy (ParaPost XH), glass fiber (ParaPost Fiber White), and zirconia (Cerapost), and to dentin.
After embedding, planar surfaces of posts (n = 9 to 14) and human dentin (n = 10) were obtained by grinding. The posts received one of three surface treatments: 1. roughening (sandblasting, hydrofluoric acid etching), 2. application of primer (Alloy Primer, Metalprimer II, silane), or 3. roughening followed by application of primer (sandblasting or etching followed by primer, Cojet treatment). ParaPost Cement and Panavia F were bonded to the post and dentin specimens, and the bonded specimens were placed in water at 37°C for 7 days. The specimens were debonded in shear.
Panavia F had significantly higher bond strength to ground ParaPost XH, Cerapost, and dentin than did ParaPost Cement. Most surface treatments resulted in an improved bond strength of resin cements to the posts. Compared to the ground control, Cojet treatment and sandblasting were the most effective treatments. Etching of Cerapost with hydrofluoric acid with and without silane treatment significantly decreased the bond strength of Panavia F to the post.
The bond strength of resin cements to the posts was affected by the material of the post, the surface treatment of the post, and by the type of resin cement. The bond strength of resin cement to dentin was influenced by the type of resin cement.