Purpose: To measure microtensile bond strength (μTBS) of universal adhesives immediately and after 6-month aging, with or without an additional adhesive layer applied on a separately light-cured or non-light-cured universal adhesive. Materials and Methods: Eighty human third molars were randomly assigned to 8 experimental groups. The universal adhesives Clearfil Universal Bond (Kuraray Noritake) and Single Bond Universal (3M Oral Care) were used in self-etch mode (following the manufacturer's directions), and either light cured or not before application of an extra hydrophobic adhesive layer (Clearfil SE Bond bond, Kuraray Noritake). The two-step self-etch adhesives Clearfil SE Bond (Kuraray Noritake) and OptiBond XTR (Kerr) were used as references. After composite buildups were bonded to mid-coronal occlusal dentin surfaces, the specimens were stored in water (37°C/24 h) and sectioned into microspecimens (0.96 ± 0.04 mm²). Half of the specimens were immediately subjected to μTBS testing (1.0 mm/min), while the other half was stored in water (37°C) for 6 months prior to testing. Failure analysis was performed using stereomicroscopy and SEM. Data were analyzed with two-way repeated measures ANOVA, Tukey's and paired t-tests (p = 0.05). Results: The immediate μTBS was similar for the universal adhesives when applied following the different application strategies (p > 0.05). Application of an extra layer of hydrophobic adhesive improved the aged μTBS of the universal adhesives, which was statistically significant when the universal adhesives were first light cured (p 0.05). The reference adhesives Clearfil SE Bond and OptiBond XTR exhibited a significantly higher immediate and aged μTBS to dentin than did the universal adhesives (p 0.05). Conclusion: The bond durability of universal adhesives, applied in self-etch mode, was found to benefit from the application of an extra hydrophobic adhesive layer when the universal adhesives were first light cured. Keywords: aging, dentin, microtensile bond strength, self-etch adhesives