Various cookies are used on our website: We use technically necessary cookies for the purpose of enabling functions such as login or a shopping cart. We use optional cookies for marketing and optimization purposes, in particular to place relevant and interesting ads for you on Meta's platforms (Facebook, Instagram). You can refuse optional cookies. More information on data collection and processing can be found in our privacy policy.
Digital extra printDOI: 10.3290/j.jad.a43996, PubMed ID (PMID): 32030380Pages 99-105, Language: EnglishLatta, Mark A. / Tsujimoto, Akimasa / Takamizawa, Toshiki / Barkmeier, Wayne W.
Purpose: To use shear bond strength (SBS) and shear fatigue strength (SFS) testing to determine the durability of adhesion of self-adhesive restorative materials compared to composite resin bonded with a universal adhesive.
Materials and Methods: A universal adhesive, Prime & Bond Active, was used in self-etch mode to bond Z-100 composite resin to enamel and dentin. Three commercially available restorative materials and one experimental material with self-adhesive properties, Activa (A), Fuji II LC(F), and Equia Forte (E) and ASAR-MP4 (S) were also bonded to enamel and dentin. The SBS and SFS were determined for all materials. A staircase method was used to determine the SFS with 10 Hz frequency for 50,000 cycles or until failure occurred.
Results: On enamel, S generated similar values to the adhesive/composite materials and higher values than F, E, and A. On dentin, the composite/universal adhesive showed significantly higher SBS and SFS than the self-adhesive materials. S, F, and E generated higher values than A on dentin.
Conclusion: SBS and SFS values to enamel were similar for all materials tested except Activa which generated lower enamel values. On dentin surfaces, the self-adhesive materials generated similar SBS and SFS, with the exception of Activa. Those values were lower than that generated with composite resin and a universal adhesive.
Keywords: adhesion to dental hard tissues, fatigue testing, glass ionomers, bond durability, self-adhesive restoratives